Formidable challenges for AFM-based functional spintronic device development are high-speed electrical manipulation (recording), detection (retrieval), and ensuring the stability of the recorded information -- all in a semiconductor industry-friendly material system.

Researchers at Tohoku University, University of New South Wales (Australia), ETH Zürich (Switzerland), and Diamond Light Source (United Kingdom) successfully demonstrated current-induced switching in a polycrystalline metallic antiferromagnetic heterostructure with high thermal stability. The established findings show potential for information storage and processing technologies.

The research group used a Mn-based metallic AFM (PtMn)/heavy metal (HM) heterostructure -- attractive because of its significant antiferromagnetic anisotropy and its compatibility with PtMn Silicon-based electronics. Electrical recording of resistance states (1 or 0) was obtained through the spin-orbit interaction of the HM layer; a charge current in the adjacent HM resulted in spin-orbit torques acting on the AFM, leading to a change in the resistance level down to a microsecond regime.

"Interestingly, the switching degree is controllable by the strength of the current in the HM layer and shows long-term data retention capabilities," said Samik DuttaGupta, corresponding author of the study. "The experimental results from electrical measurements were supplemented by a magnetic X-ray imaging, helping to clarify the reversible nature of switching dynamics localized within nm-sized AFM domains."

The results are the first demonstration of current-induced switching of an industry-compatible AFM down to the microsecond regime within the field of metallic antiferromagnetic spintronics. These findings are expected to initiate new avenues for research and encourage further investigations towards the realization of functional devices using metallic AFMs for information storage and processing technologies.

Story Source:

Materials provided by Tohoku University. Note: Content may be edited for style and length.

Journal Reference:

1. Samik DuttaGupta, A. Kurenkov, Oleg A. Tretiakov, G. Krishnaswamy, G. Sala, V. Krizakova, F. Maccherozzi, S. S. Dhesi, P. Gambardella, S. Fukami, H. Ohno. Spin-orbit torque switching of an antiferromagnetic metallic heterostructure. Nature Communications, 2020; 11 (1) DOI: 10.1038/s41467-020-19511-4